Stencil mask having main and auxiliary strut and method of forming the same

ABSTRACT

A stencil mask includes a membrane forming thin layer having membrane areas and a border area that limits the membrane areas. The membrane areas have a plurality of pattern areas which include an aperture through which particle beams can permeate and non-pattern areas interposed between the pattern areas. A main strut supports the membrane areas and is formed on the border area of the membrane forming thin layer. An auxiliary strut is formed in the non-pattern areas inside the membrane pattern area such that the auxiliary strut divides the membrane areas into plural divided membrane areas. The auxiliary strut supports the divided membrane areas.

BACKGROUND

1. Technical Field

The present disclosure relates to a stencil mask and a manufacturing method thereof, which is utilized for forming a pattern according to lithography technology using a charged particle beam such as an electron beam, and more particularly, to a stencil mask and a manufacturing method thereof using a thin film membrane supported by a strut.

2. Discussion of Related Art

As the design rule of semiconductor integrated circuit devices has decreased, lithography technologies utilizing a particle beam such as an X ray, an electron beam, and an ion beam have been developed to enhance resolution of optical instruments. Among the various types of lithography, electron beam projection lithography has an advantage of forming a fine pattern at a scale of 1 μm or less. Thus, various systems and pattern forming methods using this lithography technology have been proposed. One example is disclosed in U.S. Pat. No. 5,831,272.

Electron beam proximity projection lithography (EEL) and low energy electron beam proximity projection lithography (LEVEL) project a pattern onto a resist by permeation of the electron beam through a fine aperture formed on a stencil mask.

FIG. 1 is a perspective view of a partial composition of a conventional stencil mask 10 used in EEL or LEVEL. Referring to FIG. 1, the conventional stencil mask has a plurality of membrane areas 12 respectively patterned by a fine aperture (not shown) and divided by border areas, which are not patterned. The border areas include support struts 14 which are formed of rows and columns, which intersect perpendicularly and reinforce mechanical durability of the stencil mask 10.

FIG. 2 is a cross-section illustrating a portion of the stencil mask 10 of FIG. 1. Referring to FIG. 2, apertures 12 a corresponding to fine patterns are formed in the membrane areas 12. If electron beams 20 are projected onto the stencil mask 10, the fine pattern is projected onto a resist layer (not shown) coated on a wafer after the electron beams permeate the apertures 12 a.

The apertures 12 a are formed by etching the membrane areas 12. In a case where the fine pattern is used for manufacturing a next generation highly integrated device, for example, when the fine pattern at a scale of 0.1 μm or less is required, the apertures 12 a must be formed to have a line width on a scale of 10's of NM. In this case, the ratio of the thickness of the membrane areas 12 to the diameter of the apertures 12 a, i.e. The aspect ratio of the apertures 12 a, should be small enough to accurately form a desired profile of the apertures 12 a during etching of the membrane areas 12. Specifically, the aspect ratio of the apertures 12 a must be reasonably maintained and the thickness of the membrane areas 12 should be as thin as possible, for instance, at about 1 μm or less and preferably 500 nm or less.

However, thin membrane areas 12 bend easily, resulting in a tensile stress inside the membrane areas 12. The tensile stress causes the membrane areas 12 to transform or distort, and thus image placement error occurs since the pattern projected through the membrane areas 12 becomes displaced.

Various mask structures have been suggested to solve the above problems, such as U.S. Pat. No. 6,261,726 B1 and Japanese Patent Publication No. hei 15(2003)-59819. However, these masks, which include a structure to support the membrane, mostly use the conventional strut structure described above and thus have limitations in preventing image placement error due to the transformation or distortion of the membrane. Accordingly, there is a need for a stencil mask in which occurrence of image placement error due to transformation or distortion induced by internal stress inside membrane areas is substantially diminished without limiting size or aspect ratio of the membrane areas.

SUMMARY OF THE INVENTION

A stencil mask according to an embodiment of the invention includes a membrane forming thin layer having membrane areas and a border area that limits the membrane areas. The membrane areas include a plurality of pattern areas in which a plurality of apertures that allow permeation of particle beams is formed, and a plurality of non-pattern areas placed between the plurality of pattern areas. A main strut is formed on the border area of the membrane forming thin layer to support the membrane areas. An auxiliary strut is formed on the non-pattern areas inside the membrane areas. The auxiliary strut divides the membrane areas into a plurality of divided membrane areas and supports each divided membrane area.

In at least one embodiment of the invention, the auxiliary strut penetrates the membrane forming thin layer. The membrane forming thin layer comprises a first side opposing the main strut and a second side opposite the first side, and the second side of the membrane forming thin layer exposes a first surface of the auxiliary strut. In addition, the auxiliary strut extends by a first length from the first side of the membrane forming thin layer and the first length is shorter than a length of the main strut. Preferably, the auxiliary strut overlaps the border area and the main strut.

The stencil mask according to an embodiment of the present invention may further comprise a protection layer partially covering the auxiliary strut. The protection layer does not cover the first surface of the auxiliary strut.

A method of manufacturing a stencil mask according to an embodiment of the invention includes preparing a composite layer, the composite layer including a membrane forming thin layer having a first side and a second side opposite the first side. The membrane forming thin layer also includes a plurality of membrane areas each having a plurality of pattern areas for forming a pattern to be projected by particle beams and non-pattern areas placed between each pattern area, the non-pattern areas including a border area limiting the membrane areas. The composite layer also include a substrate having a first side facing the first side of the membrane forming thin layer and a second side opposite the first side, and an oxide layer interposed between the first side of the membrane forming thin layer and the first side of the substrate. A trench is formed by etching the composite layer in the non-pattern areas from the second side of the membrane forming thin layer. An auxiliary strut is formed by filling a support layer inside the trench, and a main strut supporting the membrane areas is formed in the border area by removing sections of the substrate included in the membrane areas.

In at least one embodiment of the invention, the main strut is formed after forming the auxiliary strut. The step of forming an auxiliary strut may further include forming a protection layer on the inside walls of the trench, and forming the support layer on the protection layer.

At least one embodiment of the invention further includes a step of forming an aperture, which penetrates the membrane forming thin layer to form a projected pattern on the pattern areas of the membrane areas. The step of forming an aperture may be performed after or before forming the main and auxiliary struts.

A method of manufacturing a stencil mask according to another embodiment of the invention includes preparing a silicon on insulator (SOI) substrate by layering sequentially a substrate, an oxide layer and a silicon thin film. A first mask pattern is formed over the silicon thin film, and a trench is formed by etching the silicon thin film, the oxide layer, and the substrate using the first mask pattern as an etching mask. An auxiliary strut is formed by filling the trench with a support layer. A second mask pattern is formed on a surface of the substrate which is opposite to a surface of the substrate which contacts the oxide layer, and a main strut which limits the membrane area of the silicon thin film is formed by etching the substrate using the second mask pattern as an etching mask. An aperture is formed which penetrates the silicon thin film to form a projected pattern inside a pattern area limited by the auxiliary strut in the membrane area.

A method of manufacturing a stencil mask according to another embodiment of the invention includes preparing a silicon on insulator (SOI) substrate by layering sequentially a substrate, an oxide layer, and a silicon thin film. A border area is arranged which limits plural membrane areas that have pattern areas and non-pattern areas, which are, placed between the pattern areas in the silicon thin film. An aperture is formed which penetrates the silicon thin film to form a projected pattern in the pattern areas. A first mask pattern is formed which covers the pattern areas having the aperture and the border area and exposes the silicon thin film in the non-pattern areas. A trench is formed by etching the silicon thin film, the oxide layer and the substrate using the first mask pattern as an etching mask, in the non-pattern areas. An auxiliary strut is formed by filling the trench with a support layer. A second mask pattern is formed on a surface of the substrate which is opposite to a surface of the substrate which contacts the oxide layer, and a main strut which limits the membrane areas is formed in the border area by etching the substrate using the second mask pattern as an etching mask.

BRIEF DESCRIPTION OF THE DRAWINGS

The present invention will become more apparent by describing in detail exemplary embodiments thereof with reference to the attached drawings in which:

FIG. 1 is a perspective view of a partial construction of a conventional stencil mask;

FIG. 2 is a fragmentary enlarged sectional view of the stencil mask of FIG. 1;

FIG. 3A is a top plan view of a stencil mask according to an embodiment of the present invention;

FIG. 3B is a bottom plan view of the stencil mask of FIG. 3A;

FIG. 3C is a cross section of the stencil mask of FIGS. 3A and 3B along a line IIIc-IIIc′ of FIGS. 3A and 3B;

FIG. 3D is a cross section of the stencil mask of FIGS. 3A and 3B along a line IIId-IIId′ of FIGS. 3A and 3B;

FIG. 4A is a top plan view of a stencil mask according to another embodiment of the present invention;

FIG. 4B is a bottom plan view of the stencil mask of FIG. 4A;

FIG. 4C is a cross section of the stencil mask of FIGS. 4A and 4B along a line IVc-IVc′ of FIGS. 4A and 4B;

FIG. 4D is a cross section of the stencil mask of FIGS. 4A and 4B along a line IVd-IVd′ of FIGS. 4A and 4B;

FIG. 5 is a plan view of a stencil mask according to another embodiment of the present invention;

FIGS. 6A through 6I are cross-sections illustrating a method of manufacturing a stencil mask according to an embodiment of the present invention; and

FIGS. 7A through 7I are cross-sections illustrating a method of manufacturing a stencil mask according to another embodiment of the present invention.

DESCRIPTION OF PREFERRED EMBODIMENTS

Various exemplary embodiments of the present invention will now be described more fully with reference to the attached drawings.

FIG. 3A is a top plan view of a stencil mask 100 according to an embodiment of the invention. FIG. 3B is a bottom plan view of the stencil mask 100. FIG. 3C is a cross-section of the stencil mask 100 along a line IIIc-IIIc′ of FIGS. 3A and 3B. FIG. 3D is a cross-section of the stencil mask 100 along a line IIId-IIId′ of FIG. 3A and FIG. 3B.

Referring to FIGS. 3A through 3D, the stencil mask 100 includes a membrane forming thin layer 110, which includes a plurality of membrane areas 110A and border areas 110B, which limit the membrane areas 110A. The size of each of the membrane areas 110A is respectively limited by a main strut 120 formed on the border areas 110B of the membrane forming thin layer 110. For instance, each membrane area 110A forms one chip area unit. The membrane forming thin layer 110 has a first side 110C facing the main strut 120 and a second side 110D on the opposite side of membrane forming thin layer 110. The first side 110C of the membrane forming thin layer 110 is observed in FIG. 3A and the second side 110D of the membrane forming thin layer 110 is observed in FIG. 3B.

Referring to FIGS. 3C and 3D, an oxide layer 122 is interposed between the border area 110B of the membrane forming thin layer 110 and the main strut 120.

Each of the membrane areas 110A has a plurality of pattern areas 114 in each of which an aperture 112 is formed, allowing particle beams (for example, electron beams) to permeate, and non-pattern areas 116 located between the pattern areas 114. An auxiliary strut 130 is formed on the non-pattern areas 116 to divide each membrane area 110A into a plurality of divided membrane areas 110Aa, 110Ab, 110Ac, 110Ad, 110Ae, and 110Af and support the divided membrane areas 110Aa, 110Ab, 110Ac, 110Ad, 110Ae, and 110Af. The divided membrane areas 110Aa, 110Ab, 110Ac, 110Ad, 110Ae, and 110Af are supported by the auxiliary strut 130, so that the pattern areas 114 may be respectively made up of a cellblock unit in which a unit cell pattern of a semiconductor memory device is clustered. In the case of the semiconductor memory device, the cell blocks are arranged in a cell type array, with a distance of about 10˜100 μm between adjacent cell blocks, and the cell arrays are separated by peripheral circuit regions with a width of about 100 μm or more. If each of the membrane areas 110A is formed to correspond to a cell array, the distance between each cellblock inside the cell array corresponds to the width of the non-pattern areas 116 placed inside each membrane area 110A. Thus, the auxiliary strut 130 is formed in the non-pattern areas 116 having a width of about 10˜100 μm. Moreover, the membrane areas 110A are separated by the border areas 110B, which have a width of about 100 μm or more. The membrane forming thin layer 110 may be made of a silicon layer. The auxiliary strut 130 is preferably formed of a material having similar stress characteristics to that of the membrane forming thin layer 110. For instance, the auxiliary strut 130 may be made of a polisilicon layer, a TiN layer, a Ti layer, or a combination layer of at least two of these three materials. The auxiliary strut 130 has a columnar shape and is preferably solid in cross section.

Referring to FIGS. 3A, 3B, and 3D, the auxiliary strut 130 is formed to penetrate the membrane forming thin layer 110, and thus, it is exposed through the second side 110D of the membrane forming thin layer 110. Furthermore, the auxiliary strut 130 has overlap portions 130 a, which extend over the border area 110B of the membrane forming thin layer 110 to partly overlap the main strut 120.

The auxiliary strut 130 extends a first length L₁ into the main strut 120, and the first length L₁ is shorter than the length L₂ of the main strut 120.

The auxiliary strut 130 is covered with a protection layer 132 excluding the side corresponding to the second side 110D of the membrane forming thin layer 110. The protection layer 132 is formed of a material that protects the auxiliary strut 130 during an etching process for forming the main strut 120, which is performed after formation of the auxiliary strut 130. For example, if the auxiliary strut 130 is formed of a polisilicon layer, the protection layer 132 is preferably made of a Ti layer, a TiN layer, a silicon nitride layer, or a combination thereof. In other embodiments of the invention, the protection layer 132 may be omitted if a sufficiently large etching selectivity difference exists between the main strut 120 and the auxiliary strut 130. For example, the protection layer 132 may be omitted if the main strut 120 is made of a silicon layer and the auxiliary strut 130 is made of a TiN or a Ti layer.

As described above, each membrane area 110A is divided into the plurality of divided membrane areas 110Aa, 110Ab, 110Ac, 110Ad, 110Ae, and 110Af corresponding to the plurality of pattern areas 114 formed by the cell block unit, and the respective divided membrane areas 110Aa, 110Ab, 110Ac, 110Ad, 110Ae, and 110Af are supported by the auxiliary strut 130 formed in the non-pattern areas 116 inside each membrane area 110A. Accordingly, it is not necessary to limit the shape and size of the main strut 120 as well as the size and aspect ratio of the membrane areas 110A. In addition, although the shape of the conventional stencil mask is restricted to that of a square lattice, the membrane areas 110A can have a variety of shapes corresponding to various circuit patterns according to the layout of the semiconductor device, which is being formed. Also, a customized stencil mask can be manufactured fitting various chip designs since the placement, width, and length of the auxiliary strut 130 can be designed in various ways according to the layout of the semiconductor or logic device.

The auxiliary strut 130 of the stencil mask according to the present embodiment of the invention is enclosed by the protection layer 132 and has a solid cross sectional shape. However, the stencil mask according to various exemplary embodiments of the present invention is not limited to this configuration.

FIGS. 4A through 4D illustrate a stencil mask 200 according to another embodiment of the present invention. FIG. 4A is a top plan view of the stencil mask 200 and FIG. 4B is a bottom plan view of the stencil mask 200. FIG. 4C is a cross-section of the stencil mask 200 along a line IVc-IVc′ of FIGS. 4A and 4B. FIG. 4D is a cross-section of the stencil mask 200 along a line IVd-IVd′ of FIGS. 4A and 4B.

Referring to FIGS. 4A through 4D, the stencil mask 200 according to the present embodiment of the invention includes an auxiliary strut 230, which has a “U” shape. The auxiliary strut 230 divides a membrane area 210A of a membrane forming thin layer 210 into a plurality of divided membrane areas 210Aa, 210Ab, 210Ac, 210Ad, 210Ae, and 210Af and supports these divided membrane areas. In this case, part of the surface of the auxiliary strut 230 exposed through the membrane forming thin layer 210 is recessed. Except for the auxiliary strut 230, the stencil mask 200 is identical to the stencil mask 100 of the previous embodiment.

FIG. 5 illustrates a stencil mask 300 according to another embodiment of the present invention. The stencil mask 300 includes membrane areas 312, 314, 316 and 318 divided into a plurality of divided membrane areas 314 a, 314 b, 316 a, 316 b, 316 c, 318 a, 318 b, 318 c, 318 d, 318 e, and 318 f supported by auxiliary struts 330 having various shapes and placements. The auxiliary strut 330 may be formed of various shapes such as a lined pattern or a lined and spaced pattern as required by the semiconductor device design.

FIGS. 6A through 6I are cross-sections illustrating a method of manufacturing a stencil mask according to an embodiment of the present invention.

Referring to FIG. 6A, a composite layer 500 is prepared by sequentially forming an oxide layer 514 and a membrane forming thin layer 520 on a substrate 512. A silicon on insulator (SOI) substrate in which the substrate 512 is made of silicon and the membrane forming thin layer 520 is formed of a silicon thin film may be used as the composite layer 500.

The membrane forming thin layer 520 has a first side 520 a, which faces the substrate 512, and a second side 520 b on the opposite side of the membrane forming thin layer 520. Moreover, the substrate 512 has a first side 512 a, which faces the membrane forming thin layer 520, and a second side 512 b on the opposite side of the first side 512 a. The oxide layer 514 is interposed between the first side 520 a of the membrane forming thin layer 520 and the first side 512 a of the substrate 512.

A hard mask layer 532 made of a silicon nitride layer or a silicon oxide layer is formed on the membrane forming thin layer 520 of the composite layer 500 and a photoresist pattern 534 is formed on the hard mask layer 532. The photoresist pattern 534 exposes the hard mask layer 532 through apertures 534 a having various widths ranging between about 10˜100 μm. The apertures 532 a may have a lined pattern or a lined and spaced pattern.

Referring to FIG. 6B, a hard mask pattern 532 a exposing the membrane forming thin layer 520 is formed by etching the hard mask layer 532 using the photoresist pattern 534 as an etching mask. Thereafter, trenches 536 a and 536 b having various widths ranging between about 10˜100 μm are formed in the substrate 512 by etching the membrane forming thin layer 520, the oxide layer 514, and the substrate 512 using the hard mask pattern 532 a and the photoresist pattern 534 as the etching mask. The trenches 536 a and 536 b do not completely penetrate the substrate 512.

Referring to FIG. 6C, after removing the photoresist pattern 534, a protection layer 540 is formed on the inside walls of the trenches 536 a and 536 b and an upper surface of the hard mask pattern 532 a, and a support layer 550 is formed on the surface of the protection layer 540 to fill the trenches 536 a and 536 b.

The protection layer 540 protects the support layer 550 when etching the substrate 512 in a subsequent process and may be formed of a Ti layer, a TiN layer, a silicon nitride layer or a combination layer made of two or more of these three materials. The support layer 550 is necessary for forming the auxiliary strut and may be formed of a polisilicon layer, a TiN layer, a Ti layer, or a combination layer made of two or more of these three materials. In the case where the support layer 550 is made of a TiN layer, a Ti layer, or a combination thereof, the protection layer 540 may be omitted.

In addition, the trench 536 a having a relatively small width is completely filled in by the support layer 550 and the trench 536 b having a relatively large width is partially filled in by the support layer 550.

Referring to FIG. 6D, support layer patterns 550 a and 550 b composing the auxiliary strut inside the trenches 536 a and 536 b are formed by removing the support layer 550 at the outside of the trenches 536 a and 536 b using chemical mechanical polishing (CMP) or etchback methods. As a result, a support layer pattern 550 a completely filling the inside of the trench 536 a gives the auxiliary strut a columnar shape, and a support layer pattern 550 b having part of its surface 550 c recessed gives the auxiliary strut a U-shape.

If the etchback method is used to remove the support layer 550 at the outside of the trenches 536 a and 536 b, a sacrificial layer made of a flowable oxide (FOX) layer or a spin on glass (SOG) layer is formed on the support layer 550 to protect the recessed part of the support layer pattern 550 b during the etchback process, and the sacrificial layer is removed after the etchback process is performed.

Referring to FIG. 6E, a photoresist pattern 560 is formed on the second side 512 b of the substrate 512. The photoresist pattern 560 is formed on a border area, which limits a membrane area that will be formed on the membrane forming thin layer 520.

Referring to FIG. 6F, the substrate 512 is etched using the photoresist pattern 560 as the etching mask. Thereafter, only the sections of the substrate 512 corresponding to membrane areas 522 of the membrane forming thin layer 520 are removed, and main struts 512 a which support the membrane area 522 on border areas 524 are formed by the remaining sections of the substrate 512.

Referring to FIG. 6G, after the photoresist pattern 560 is removed, an exposed portion of the oxide layer 514, the protection layer 540 and the hard mask pattern 532 a are removed by a wet or dry etching method and the second side 520 b of the membrane forming thin layer 520 is exposed via a planarizing process. As a result, each of the membrane areas 522 is respectively divided into a plurality of divided membrane areas 522 a and 522 b by the auxiliary strut, which includes the support layer pattern 550 a and 550 b formed on non-pattern areas of each of the membrane areas 522. A structure wherein the respective divided membrane areas 522 a and 522 b are supported by the auxiliary strut, which includes the support layer patterns 550 a and 550 b is obtained. The divided membrane areas 522 a and 522 b each include a pattern area in which a projected pattern is formed by particle beams. Here, the auxiliary strut which includes the support layer patterns 550 a and 550 b has a length L₃, from the first side 520 a of the membrane forming thin layer 520, that is shorter than a length L₄ of the main strut 512 a.

Referring to FIG. 6H, a photoresist pattern 570, which leaves part of the divided membrane areas 522 a and 522 b exposed, is formed on the second side 520 b of the membrane forming thin layer 520.

Referring to FIG. 6I, a plurality of apertures 526 which penetrate the membrane forming thin layer 520 are formed by etching the membrane forming thin layer 520 in the divided membrane areas 522 a and 522 b using the photoresist pattern 570 as the etching mask.

FIGS. 7A through 7I are cross-sections illustrating a method of manufacturing a stencil mask according to another embodiment of the present invention. The present embodiment is similar to the previous embodiment except an aperture penetrating the membrane forming thin layer is formed before an auxiliary strut is formed. Therefore, in the description of this embodiment, a detailed explanation of steps corresponding to the previous embodiment is omitted.

Referring to FIG. 7A, a composite layer 600 is prepared by sequentially layering a substrate 612, an oxide layer 614, and a membrane forming thin layer 620. In the event that the composite layer 600 is made of the SOI substrate, the substrate 612 is made of silicon and the membrane forming thin layer 620 is formed of a silicon thin film.

Thereafter, a plurality of membrane areas, which have pattern areas, and non-pattern areas in the membrane forming thin layer 620, and a border area limiting the membrane areas are formed. After forming a photoresist pattern 630 on the membrane forming thin layer 620, a plurality of apertures 626, which penetrate the membrane forming thin layer 620, are formed by etching the membrane forming thin layer 620 using the photoresist pattern 630 as the etching mask.

Referring to FIG. 7B, the photoresist pattern 630 is removed. Thereafter, a hard mask layer 632 made of a silicon nitride layer or a silicon oxide layer is formed inside the apertures 626 and on the membrane forming thin layer 620.

Referring to FIG. 7C, a photoresist pattern 634 is formed on the hard mask layer 632. The photoresist pattern 634 exposes the hard mask layer 632 through apertures having various widths ranging between about 10˜100 μm. A hard mask pattern 632 a which exposes sections of the non-pattern areas of the membrane forming thin layer 620 and simultaneously covers the pattern areas and the border areas is formed by etching the hard mask layer 632 using the photoresist pattern 634 as the etching mask.

Referring to FIG. 7D, trenches 636 a and 636 b having various widths ranging between about 10˜100 μm in the substrate 612 are formed by etching the membrane forming thin layer 620, the oxide layer 614, and the substrate 612 using the hard mask pattern 632 a and the photoresist pattern 634 as the etching mask. The trenches 636 a and 636 b do not completely penetrate the substrate 612.

Referring to FIG. 7E, after removing the photoresist pattern 634, a protection layer 640 is formed on the inside walls of the trenches 636 a and 636 b and an upper surface of the hard mask pattern 632 a, and a support layer 650 is formed on the protection layer 640 to fill the trenches 636 a and 636 b.

The protection layer 640 may be formed of a Ti layer, a TiN layer, a silicon nitride layer or a combination layer made of two or more of these three materials. The support layer 650 may be formed of a polisilicon layer, a TiN layer, a Ti layer, or a combination layer made of two or more of these three materials. In the case that the support layer 650 is made of a TiN layer, a Ti layer, or a combination thereof, the protection layer 640 may be omitted.

In addition, the trenches 636 a that have a relatively small width are completely filled in by the support layer 650 and the trench 636 b that has a relatively large width is partially filled in by the support layer 650.

Referring to FIG. 7F, support layer patterns 650 a and 650 b which form the auxiliary strut inside the trenches 636 a and 636 b are formed by removing the support layer 650 outside of the trenches 636 a and 636 b by a CMP or an etchback method. As a result, the support layer pattern 650 a is formed to completely fill the inside of the trench 636 a, which gives the auxiliary strut a columnar shape, and the support layer pattern 650 b is formed with part of its surface 650 c recessed, which gives the auxiliary strut a U-shape.

Referring to FIG. 7G, a photoresist pattern 660 is formed on a surface 612 b of the substrate 612 which faces away from the membrane forming thin layer 620. The photoresist pattern 660 is formed on border areas which limit a membrane area that will be formed on the membrane forming thin layer 620.

Referring to FIG. 7H, the substrate 612 is etched using the photoresist pattern 660 as the etching mask. As a result, only the section of the substrate 612 corresponding to a membrane area 622 of the membrane forming thin layer 620 is removed and a main strut 612 a which supports the membrane area 622 on the border area 624 remains.

Referring to FIG. 7I, after removing the oxide layer 614, exposed sections of the protection layer 640, and the hard mask pattern 632 a are removed by a wet or dry etching method and the membrane forming thin layer 620 is exposed by a planarizing process. As a result, the membrane area 622 is divided into a plurality of divided membrane areas 622 a, 622 b, 622 c, and 622 d by the auxiliary struts which include the support layer patterns 650 a and 650 b formed on the non-pattern areas of the membrane areas 622. The respective divided membrane areas 622 a, 622 b, 622 c, and 622 d are supported by the auxiliary struts which include the support layer pattern 550 a and 550 b. The respective divided membrane areas 622 a, 622 b, 622 c, and 622 d include apertures 626 of the pattern areas. The auxiliary strut formed of the support layer patterns 650 a and 650 b has a length L₅, from a first side 620 a of the membrane forming thin layer 620, that is shorter than a length L₆ of the main strut 612 a.

A stencil mask according to various exemplary embodiments of the present invention has various types of auxiliary struts placed inside membrane areas which are limited by a main strut. Moreover, the stencil mask according to exemplary embodiments of the present invention is particularly useful for patterning a locally densified pattern area such as a cell array area of a semiconductor memory device. Relatively large membrane areas are supported not only by a main strut, but also by an auxiliary strut formed in non-pattern areas. Accordingly, transformation or distortion of the membrane areas is prevented and image placement error can be minimized. A decline in the pattern's location precision can also be prevented.

Furthermore, the placement, width and length of an auxiliary strut can be designed in various ways according to the layout of the semiconductor memory or the logic device, for which the stencil mask is used. Thus, a customized stencil mask which fits various chip layouts can be manufactured without limitation in the shape and placement of the main strut and the size and aspect ratio of the membrane areas.

While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it will be understood by those of ordinary skill in the art that various changes in form and details may be made therein without departing from the spirit and scope of the present invention as defined by the following claims. 

1. A stencil mask comprising: a membrane forming thin layer comprising: membrane areas, each membrane area including a plurality of pattern areas in which a plurality of apertures that allow permeation of particle beams is formed, and a plurality of non-pattern areas placed between the plurality of pattern areas; and a border area which limits the membrane areas; a main strut formed on the border area of the membrane forming thin layer to support the membrane areas; and an auxiliary strut formed on the non-pattern areas inside the membrane areas, the auxiliary strut dividing the membrane areas into a plurality of divided membrane areas and supporting each divided membrane area.
 2. The stencil mask of claim 1, wherein the auxiliary strut penetrates the membrane forming thin layer.
 3. The stencil mask of claim 1, wherein the membrane forming thin layer comprises a first side opposing the main strut and a second side opposite the first side, and the auxiliary strut has a surface exposed through the second side.
 4. The stencil mask of claim 1, wherein the auxiliary strut extends by a first length from the first side of the membrane forming thin layer and the first length is shorter than a length of the main strut.
 5. The stencil mask of claim 1, wherein the auxiliary strut overlaps the border area and the main strut.
 6. The stencil mask of claim 1, wherein the membrane forming thin layer is made of a silicon layer and the auxiliary strut is made of a material selected from the group consisting of a polisilicon layer, a TiN layer, a Ti layer, and a combination layer made of two or more of these three materials.
 7. The stencil mask of claim 1, further comprising a protection layer partially covering the auxiliary strut.
 8. The stencil mask of claim 7, wherein the membrane forming thin layer comprises a first side opposing the main strut and a second side opposite the first side, the second side of the membrane forming thin layer exposes a first surface of the auxiliary strut, and the protection layer does not cover the first surface of the auxiliary strut.
 9. The stencil mask of claim 7, wherein the protection layer is made of a material selected from the group consisting of a Ti layer, a TiN layer, a silicon nitride layer, and a combination layer made of two or more of these three materials.
 10. The stencil mask of claim 1, further comprising an oxide layer interposed between the border area of the membrane forming thin layer and the main strut.
 11. The stencil mask of claim 1, wherein the auxiliary strut has a solid cross section and a columnar shape.
 12. The stencil mask of claim 1, wherein the membrane forming thin layer has a first side facing the main strut and a second side partially exposing a first surface of the auxiliary strut, and part of the first surface is recessed such that the auxiliary strut has a “U” shape.
 13. The stencil mask of claim 1, wherein the auxiliary strut is located in the non-pattern areas of the membrane forming thin layer such that the membrane areas are divided into a plurality of divided membrane areas sectioned by a cellblock unit.
 14. A stencil mask comprising: a membrane forming thin layer having membrane areas and a border area that limits the membrane areas; a main strut formed on the border area of the membrane forming thin layer that supports the membrane areas; and an auxiliary strut formed inside the membrane areas that divides the membrane areas into a plurality of divided membrane areas and supports the plurality of divided membrane areas.
 15. The stencil mask of claim 14, further comprising a plurality of apertures formed in the membrane areas. 